AZS ramming mass is an unformed refractory material composed of fused zirconia corundum particles and a small amount of additives. The product is easy to use, hardens at room temperature, has high refractoriness and high compressive strength, has small thermal expansion and contraction, and has strong corrosion resistance to glass liquid. AZS ramming mass is the most ideal unformed refractory material for bottom seal of glass furnace. Its construction process includes checking the wetting or hardening of the coagulant, mixing it evenly according to the proportion, and then adding room temperature water according to the site conditions to stir until there is no remaining raw material, and then flattening it by vibration.
1. Easy to use: easy to construct, can be hardened at room temperature, and the construction process is simple and efficient.
2. High refractoriness: It has excellent fire resistance and is suitable for use in high temperature environments.
3. High compressive strength: The hardened material has high compressive strength, ensuring long-term stable use.
4. Small thermal expansion: The material has small thermal expansion and contraction, which reduces structural deformation caused by temperature changes.
5. Strong corrosion resistance: It has excellent corrosion resistance to glass liquid and prolongs the service life of the equipment.
6. Environmentally friendly and pollution-free: It does not contain phosphorus, has no pollution to the environment, and meets green environmental protection requirements.
7. Reusable: The remaining mixture can be reused in the wet state to improve material utilization.
1. Laying on the bottom of glass kiln: used for refractory laying on the bottom of kiln, providing good thermal insulation effect.
2. Melting end and working area: Suitable for fire resistant protection of melting end and working area to improve fire resistance performance.
3. Brick joint treatment: used to fill the joints between brick layers to enhance structural stability.